Contact us Polyimide Film BOPI (similar to kapton HN)

BOPI (similar to Kapton HN)

Kapton FN BOPI

Properties

BOPI (Biaxial Oriented Polyimide film, similar to Kapton HN) is achieved by polycondensation of PMDA and ODA in strong polar solvents, through the process of film forming, and then being stretched and Oriented by biax during the course of imine at high temperature. BOPI film is a special kind of Polyimide film, however, as the result of Biaxial Orientation, BOPI film possesses higher physical, chemical, and electrical properties, which performs successfully in the wide range of temperature as low as -452F(-269c) and as high as +500F(+260c) and can be exposed at +752F(400c) in short time, besides, it is of atomic radiation resistant. BOPI film is currently the macromolecular compound with the best combined properties and the highest heat resistant.      

Data Form

Item

Properties

Unit

Values

μm

25

30

40

50

75

1

Density

g/cm3

142020

2

Tensile Strength

MD ≥

MPa

185

175

160

155

150

TD ≥

170

160

150

140

135

3

Elongation at rapture  ≥

%

60

4

Shrinkage

(only for reference)

150℃ 30min ≤

%

0.15

400℃ 30min ≤

2.0

5

Breakdown

Strength(48~62Hz)

Average

MV/m

210

190

170

160

150

Individual

190

180

160

135

120

6

*Surface Resistance  200

Ω

≥1.01013

7

*Volume Resistance  200

Ωm

≥1.01010

8

*Dielectric Constant (4862Hz)

---

3.5

9

*Loss Tangent (4862Hz)

---

≤0.004

The items marked * are the inherent properties of Polyimide Film, which are not showed on the testing report for outgoing factory.

Specification

1. Width: 1000mm,or Slit into tapes; Thickness tolerance: +-10%
2. Min Qty: 200kgs each size in a lot. Packing: 25--50 Kgs/carton.

Note: The values noted in above technical specification are given only for our customers’ reference and should not be used in writing specifications.

 